The scientists found that UV exposure in PERC and TOPCon solar cells increases interface defects and makes them more recombination…
Researchers from the University of New South Wales and Jolywood found that corrosion-induced degradation in TOPCon solar cells is mainly…
UNSW research shows tracker-based PV systems experience higher UV degradation than fixed-tilt arrays
New research from the University of New South Wales shows that the degradation of PV modules varies widely depending on…
UNSW researchers developed a chemically selective, nitrate-based, single-sided accelerated aging method for TOPCon solar cells that replicates the mildly acidic…
A global study shows that climate change will sharply increase the risks of high temperatures, accelerate degradation and increase the…
Researchers in the Netherlands have developed a model to identify acceptable top cell degradation rates in perovskite-silicon tandem modules. Simulations…
NREL researchers found that UV exposure can cause significant, some of it non-repairable degradation in TOPCon solar cells, with strong…
SUPSI researchers found that six Swiss PV systems installed in the late 1980s and early 1990s exhibit exceptionally low degradation…
Scientists from the French research institute CEA-Liten have identified hydrogen migration in doped selective layers as the main driver of…
Thicker aluminum oxide layers can reduce ultraviolet-induced degradation in TOPCon solar cells – SPE
UNSW researchers developed an experimentally validated model that links UV-induced degradation in TOPCon solar cells to hydrogen transport, charge capture…